Influência do croma do substrato e da espessura de material cerâmico na cor de cerâmicas injetadas

Vol. 5 – Número 17 – 2015 Artigo original / Original article  Página 39-43 Influência do croma do substrato e da espessura de material cerâmico na cor de cerâmicas injetadas Influence of the substrate chroma and ceramic thickness on the color of heat-press ceramics Danielle Lacerda1  Analucia Philippi2 Elisa Oderich3 Claudia Volpato4 Resumo Este estudo teve por objetivo avaliar a influência óptica do croma do substrato e de diferentes espessuras de material na cor de cerâmicas injetadas. Dez discos cerâmicos foram confeccionados em cerâmica injetada à base de leucita (IPS Empress Esthetic) em duas espessuras (1,0 e 2,0 mm). Três discos, relativos aos substratos foram confeccionados em resina composta, com o mesmo matiz, porém, com croma gradual (A2, A3 e A4). Cada disco cerâmico foi posicionado sobre um fundo cinza neutro e as coordenadas L* a* b* foram mensuradas com um dispositivo de mensuração de cor intraoral. As médias resultantes dessas medidas foram usadas como medidas de referência (L*:81,3, a*:-0,46, b*:22,04). Após, os discos cerâmicos foram sobrepostos aos discos dos substratos e três mensurações foram realizadas para cada associação. As coordenadas de luminosidade (L*) e cromaticidade (a* e b*) das associações experimentais foram usadas para o cálculo das diferenças de cor (ΔE) para a espessura de 1,0 mm (A2: 4,69; A3: 4,13 e A4: 4,22ΔE) e para 2,0 mm (A2: 1,11; A3: 1,30 e A4: 1,12ΔE). A análise estatística foi realizada pelo teste ANOVA a dois critérios e as comparações múltiplas pelo teste de Tukey (p<0,05). Diferenças estatísticas foram encontradas entre as espessuras testadas (p<0,001), demonstrando que os discos de cerâmica com espessura de 2,0 mm apresentaram as menores diferenças de cor. As mudanças no croma do substrato não foram capazes de influenciar a cor final da cerâmica (p<0,84). Descritores: Cor, cerâmica. Abstract This study evaluated the optical influence of the substrate chroma and of different ceramic thickness on the color of heat-pressed ceramics. Ten ceramic discs were made of leucite-based injected ceramic (IPS Empress Esthetic), color TC1, in two thickness (1.0 and 2.0mm). Three discs, for the substrates, were made of composite resin, with the same hue, but with gradual chroma (A2, A3 and A4). Each ceramic disc was positioned on a neutral background and coordinates L*a*b* were measured with an intraoral color measurement device. The average result of these measures were used as the average standard (L*: 81.3; a*: -0.46; b*: 22.04). After, the ceramic discs were overlaid on the disks of the substrates and three measurements were performed for each association. The coordinates of lightness (L*) and cromaticity (a* and b*) of experimental combinations were used to calculate the color difference (ΔE) for the thickness 1.0mm (A2: 4.69; A3: 4.13 and A4: 4.22ΔE) and 2.0mm (A2: 1.11; A3: 1.30 and A4: 1.12ΔE). The statistical analysis was performed by two-way ANOVA, and multiple comparisons were made by Tukey’s Test (p <0.05). Statistical differences were found between the tested thicknesses (p<0.001), demonstrating that the ceramic discs with 2.0 mm showed the smallest color differences. The changes in chroma were not able to influence the final color of the ceramic (p<0.84). Descriptors: Color, ceramics. 1 Graduação em Odontologia, Mestranda em Odontopediatria – UFSC. 2 Ma., Profª. – UFSC. 3 Dra. em Odontologia/Implantodontia – UFSC, Profª. Adjunta do Departamento de Odontologia – UFSC. 4 Dra. em Odontologia – Dentística Restauradora/Implantodontia – UFSC,  Profª. Associada do Departamento de Odontologia – UFSC.