Dureza e grau de conversão de resinas polimerizadas por halógeno e LED

Dureza e grau de conversão de resinas polimerizadas por halógeno e LED

Vol. 8 – Número 32 – 2017   CADERNO DE ODONTOLOGIA CLÍNICA   Artigo original/Original article   Página 90-95 Dureza e grau de conversão de resinas polimerizadas por halógeno e LED Hardness and degree of conversion of composite polymerized with halogen and LED   Lidiane Cristina Machado Costa1 João Batista Novaes Júnior2  Ivan Doche Barreiros2 Elissa Talma3   Resumo Este estudo objetivou determinar a dureza Vickers e o grau de conversão de uma resina composta polimerizadas por halógeno e LED em diferentes profundidades (2,0 e 3,0 mm). Foram utilizados os aparelhos XL3000 (halógeno – 3M) e Bright Lec (LED – MM Optics). Os corpos de prova mediam 2 e 3 mm de altura e foram divididos em 4 grupos (n=8). G1: 2 mm-halógeno; G2: 2 mm-LED; G3: 3 mm-halógeno e G4: 3 mm-LED. Os corpos de prova foram submetidos ao teste de dureza Vickers, sendo que cada amostra recebeu cinco indentações (200 g durante 6 segundos), e foi medido o grau de conversão com o espectrômetro de infravermelho (Fourier). A média dos resultados da dureza Vickers (G1: 33,64; G2: 26,60; G3: 22,71; e G4: 15,46) foi submetida à análise estatística (ANOVA), e não apresentaram diferença estatisticamente significante na profundidade de 2 mm. Na profundidade de 3 mm a tecnologia halógena apresentou resultado estatisticamente superior à tecnologia LED (p<0,05). Os dados obtidos no espectrômetro de infravermelho foram submetidos à análise estatística (testes T). Os resultados do grau de conversão não diferiram estatisticamente. As médias de grau de conversão foram: G1: 65,9%; G2: 66,0%; G3: 68,4% e G4: 67,5%. Assim, conclui-se que a dureza diminuiu com o aumento da profundidade para as diferentes tecnologias emissoras de luz, e na profundidade de 3,0 mm o aparelho halógeno apresentou resultado superior ao aparelho LED. O grau de conversão não foi afetado pela profundidade e pela emissão de luz.   Descritores: Dureza, resina composta, grau de conversão, fotopolimerização.   Abstract This study aimed to evaluate the Vickers hardness and the degree of conversion of a resin composite cured by two polymerized with different technology of emission of light (halogen and LED) in different depth (2 and 3 mm). Devices were used XL3000 (halogen – 3M  ) and Bright Lec (LED – MM Optics). The specimens measured 2 and 3 mm in height and were divided into 4 groups (n = 8). G1: 2 mm-halogen; G2: 2 mm-LED; G3: 3 mm-halogen; and G4: 3 mm-LED. The samples were submitted to Vickers hardness test, each sample received five indentations (200 g for 6 seconds), and measured the degree of conversion with the infrared spectrometer (Fourier). The average of the results of Vickers hardness (G1: 33.64; G2: 26.60; G3: 22.71; and G4: 15.46) was subjected to statistical analysis (ANOVA) and showed no statistically significant difference at a depth of 2 mm. In the depth of 3 mm halogen technology presented was statistically superior to LED (p <0.05). Data from the infrared spectrometer have been subjected to statistical analysis (T test). The results of the degree of conversion did not differ statistically. The average degree of conversion was: G1: 65.9%; G2: 66.0%; G3: 68.4%; and G4: 67.5%. It was concluded that the hardness decreased with increasing depth for the different technologies emitting light, and 3.0 mm in depth of the halogen unit provides results superior to the LED device. The degree of conversion was not affected by the depth and light emission.   Descriptors: Hardness, resin composites, conversion degree, polymerization.   1 Profª. Titular de Periodontia – Centro Universitário Newton Paiva, Drª. em Periodontia – FO/UFMG. 2 Prof. Associado de Clínica Integrada – FO/UFMG. 3 Doutoranda em Biomecânica – Engenharia de estruturas – Escola de Engenharia/UFMG. 

Este contenido está restringido a los miembros del sitio. Si eres un usuario existente, por favor, accede. Los nuevos usuarios pueden registrarse a continuación.

Acceso de usuarios existentes
   
Registro de un nuevo usuario
*Campo necesario
Abrir conversa
Precisa de ajuda?