Análise de falhas adesivas à zircônia ….

  CADERNO DE PRÓTESE Ano 2, Volume 8 – 2011 Artigo original (Article original) Página 383-387 Análise de falhas adesivas à zircônia sob diferentes tratamentos de superfície após ensaio de microtração. Zirconia failure analysis under different surface treatment after microtensile experiment. Ricardo Alexandre Zavanelli¹ Fabiana Marques Guimarães² Jaqueline Barbosa Magalhães³ Van Purdy Thompson4 Nelson Renato França Alves da Silva5 Resumo Considerando a importância do procedimento de cimentação adesiva para as restaurações indiretas, o propósito desse estudo foi analisar o tipo de falha ocorrida sob diferentes tratamentos de superfície e após ensaio de microtração entre dois substratos (zircônia Y-TZP e resina composta). Assim, 16 blocos (12mm X 12mm X 4mm) de uma zircônia completamente sinterizada foram polidos e divididos em 04 grupos de acordo com o tratamento de superfície a ser realizado sobre a zircônia: jateamento (G1), jateamento + “primer universal” (G2), “primer universal” (G3), e NaOH + “primer universal” (G4), previamente ao procedimento de cimentação. Os blocos de zircônia foram cimentados aos blocos de resina composta (12mm X 12mm X 4mm) previamente confeccionados e fotopolimerizados para em seguida serem cortados sob abundante refrigeração a fim de produzir secções de 0,8mm X 0,8mm X 8mm. Os “palitos” obtidos foram ensaiados em máquina universal de ensaios para detectar o tipo de falha ocorrida, que foi classificada em adesiva, coesiva ou mista. Os resultados evidenciaram uma maior percentagem de falhas mistas para os grupos G2 e G4 (65,2% e 67,3%, respectivamente), enquanto que o G3 apresentou maior percentagem de falhas adesivas (75,6%). Concluiu-se que o tratamento de superfície com jateamento com óxido de alumínio sobre a superfície da zircônia (G1) não é recomendado para a zircônia do tipo Y-TZP. Descritores: Falhas, zircônia, tratamento de superfície. Abstract Considering the importance of the adhesive cementation procedure for indirect restoration, the aim of this study was to analyze the failure kind met under different surface treatment and after microtensile test between two substrates (zirconia Y-TZP and resin composite). In this way, 16 blocks (12mm X 12mm X 4mm) of a zirconia completely sintering were polished and divided into 04 groups according to the surface treatment to be executed over the zirconia: sandblast (G1); sandblast + universal primer (G2); universal primer (G3); NaOH + universal primer (G4), previously to the cementation procedure. The zirconia blocks were cemented into the resin composite blocks (12mm X 12mm X 4mm) previously done and photopolimerized, to be in the sequence cut under copious refrigeration to produce sections of approximately 0.8mm x 0.8mm X 0.8mm. These obtained sticks were tested in a universal machine to detect the kind of failure, which was classified in adhesive, cohesive or mix. The results showed a higher percentage of mix failure to the group G2 and G4 (65.2% e 67.3%, respectively), while the group G3 showed a higher percentage of adhesive failure (75.6%). It was concluded that the sandblast treatment surface with aluminum oxide over the zirconia surface wasn’t recommended to the Y-TZP zirconia. Descriptors: Failures, zirconia, surface treatment. ¹Prof. Associado da Disciplina de Prótese Dentária do Depto de Prevenção e Reabilitação Oral da Faculdade de Odontologia da Universidade Federal de Goiás. ²Discente e Bolsista do PIBIC/CNPq da Faculdade de Odontologia da Universidade Federal de Goiás. ³Discente e Bolsista do PIBIC/CNPq da Faculdade de Odontologia da Universidade Federal de Goiás. 4Prof. do Departamento de Biomateriais e Biomimética da Faculdade de Odontologia da Universidade de Nova Iorque. 5Prof. do Departamento de Prótese da Faculdade de Odontologia da Universidade de Nova Iorque.